Styrolution Luran® S 776 S Colored ASA

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer Styrolution
Trade Name Luran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® S 776 S Colored ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection molding grade with good toughness and strength. Uses include parts for garden equipment, parts for office chairs and antennas.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Water Absorption 1.65 %
1.65 %
Equilibrium; ISO 62
0.45 %

@Time 86400 sec
0.45 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.35 %
0.35 %
23°C/50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Melt Flow 4.28 g/10 min

@Load 10.0 kg,
Temperature 220 °C
4.28 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 70.0 MPa

@Load 36.5 kg,
Time 30.0 sec
10200 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 47.0 MPa
6820 psi
50 mm/min; ISO 527-1/-2
Elongation at Break 12 %
12 %
Nominal, 50 mm/min; ISO 527-1/-2
Elongation at Yield 3.3 %
3.3 %
50 mm/min; ISO 527-1/-2
Tensile Modulus 2.20 GPa
319 ksi
ISO 527-1/-2
Flexural Strength 65.0 MPa
9430 psi
ISO 178
Izod Impact, Notched 2.85 J/cm
5.34 ft-lb/in
ASTM D256
Charpy Impact Unnotched 15.0 J/cm²

@Temperature -30.0 °C
71.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
27.0 J/cm²

@Temperature 23.0 °C
128 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 1200 MPa

@Strain <=0.500 %
174000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 - 110 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.4 - 61.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
DIN 52612-1
Maximum Service Temperature, Air 80.0 °C
176 °F
Deflection Temperature at 0.46 MPa (66 psi) 101 °C
214 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 96.0 °C
205 °F
ISO 75-1/-2
Vicat Softening Point 92.0 °C
198 °F
VST/B/50; ISO 306
104 °C
219 °F
VST/A/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Diameter 4.00 mm
HB

@Diameter 0.157 in
IEC 60707
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
IEC 60250
3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
K20/P20; IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
0.0090

@Frequency 100 Hz
IEC 60250
0.034

@Frequency 1.00e+6 Hz
0.034

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test Liquid A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Injection
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Injection
Drying Temperature 80.0 °C
176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Pre-drying
Descriptive Properties Value Comments
Color Black 71200
Gray 00148
Natural
White 00260
Commercial Status Europe
Primary Processing Technique Injection Molding