- Acrylonitrile/Styrene/Acrylate (ASA), 15% Glass Reinforced
- Styrolution Luran® S KR 2858 GS Colored 15% Glass Filled ASA
Styrolution Luran® S KR 2858 GS Colored 15% Glass Filled ASA
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), 15% Glass Reinforced |
| Manufacturer | Styrolution |
| Trade Name | Luran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Luran® S KR 2858 GS Colored 15% Glass Filled ASA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass-reinforced grade with high stiffness and heat distortion resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 1.42 % | 1.42 % | Equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | 23°C/50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Melt Flow | 5.9 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.9 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa @Load 36.5 kg, Time 30.0 sec |
24700 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | Nominal, 50 mm/min; ISO 527-1/-2 |
| Tensile Modulus | 6.60 GPa | 957 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 2.80 J/cm² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75-1/-2 |
| Vicat Softening Point | 115 °C | 239 °F | VST/B/50; ISO 306 |
| 120 °C | 248 °F | VST/A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | Injection Molding |
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Pre-drying |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black 56626 | |
| Gray 36878 | ||
| Natural | ||
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Network Polymers Softflex® 2701T Transparent
- Materion BrushBronze® 630 (AMS 4640) 3.0" - 5.0"
- LG Chemical LUPOY GN2101FC PC+GF10%, Halogen Free, Flame Retardant, Heat Resistance
- LG Chemical SEETEC BF415 LDPE
- Shandong Dongyue Shenzhou New Material Co DS601 Perfluorinated Ethylene-Propylene Copolymer
- A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6
- Dow Corning SILASTIC® 7-6840 BIOMEDICAL GRADE LSR, KIT
- Eastman Eastman AP007 Copolyester
- ChevronTexaco Delo® NLGI 2 Grease EP
- 3M 519YS Sandblast Stencil Products
Copyright © lookpolymers.com All Rights Reserved