Styrolution Luran® S KR 2861/1 C Colored ASA+PC

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer Styrolution
Trade Name Luran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® S KR 2861/1 C Colored ASA+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Grade with high heat resistance for injection molding and extrusion.Applications: Interior and exterior automotive parts, and electrical housings.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Water Absorption 0.90 %
0.90 %
Equilibrium; ISO 62
0.30 %

@Time 86400 sec
0.30 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.25 %
0.25 %
23°C/50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0070 cm/cm
0.0030 - 0.0070 in/in
Melt Flow 16.24 g/10 min

@Load 5.00 kg,
Temperature 260 °C
16.24 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 95.0 MPa

@Load 36.5 kg,
Time 30.0 sec
13800 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 53.0 MPa
7690 psi
50 mm/min; ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
Nominal, 50 mm/min; ISO 527-1/-2
Elongation at Yield 4.9 %
4.9 %
50 mm/min; ISO 527-1/-2
Tensile Modulus 2.30 GPa
334 ksi
ISO 527-1/-2
Flexural Strength 78.0 MPa
11300 psi
ISO 178
Poissons Ratio 0.28
0.28
Calculated
Shear Modulus 0.900 GPa
131 ksi
ISO 6721-2
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 1600 MPa

@Strain <=0.500 %
232000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 - 90.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 - 50.0 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
DIN 52612-1
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 0.46 MPa (66 psi) 125 °C
257 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 106 °C
223 °F
ISO 75-1/-2
Vicat Softening Point 120 °C
248 °F
VST/B/50; ISO 306
136 °C
277 °F
VST/A/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Diameter 4.00 mm
HB

@Diameter 0.157 in
IEC 60707
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
IEC 60250
Dielectric Strength 38.0 kV/mm
965 kV/in
K20/P20; IEC 60243-1
Dissipation Factor 0.0060

@Frequency 100 Hz
0.0060

@Frequency 100 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
Test Liquid A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 280 °C
482 - 536 °F
Extrusion, Plates
260 - 300 °C
500 - 572 °F
Injection Molding
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Injection Molding
Drying Temperature 100 - 110 °C
212 - 230 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Pre-drying
Descriptive Properties Value Comments
Color Black 35914
Black 89828
Natural
White 31425 Q105
Commercial Status Europe
Primary Processing Technique Injection Molding and Extrusion