Styrolution PS 485N HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 485N HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 485N is a high impact grade of polystyrene for extruded sheets with a matte surface.Matte SurfaceUL 94 HBInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ISO 527 |
| Elongation at Break | 35 % | 35 % | ISO 527 |
| Elongation at Yield | 1.6 % | 1.6 % | ISO 527 |
| Tensile Modulus | 1.65 GPa | 239 ksi | ISO 527 |
| Flexural Strength | 32.0 MPa | 4640 psi | ISO 178 |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Vicat Softening Point | 90.0 °C @Load 5.10 kg |
194 °F @Load 11.2 lb |
120°C/h; ASTM D 1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 |
| Dissipation Factor | 0.00040 @Frequency 100 Hz |
0.00040 @Frequency 100 Hz |
IEC 60250 |
| 0.00040 @Frequency 1.00e+6 Hz |
0.00040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | ISO 294 |
| Mold Temperature | 45.0 °C | 113 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Crastin® LW9320LM BK591 PBT (Unverified Data**)
- Hybrid Plastics POSS® MA0735 MethacrylPhenyl-POSS® Cage Mixture
- Shakespeare FL-8 Fluorocarbon PVDF Fishing Line, 25 lb
- Solvay Specialty Polymers Polymist® XPP 511 Polytetrafluoroethylene (PTFE)
- Polyplastics Duranex® 7307B Polybutylene Terephthalate (PBT), Super low warpage, GB filled
- ExxonMobil Enable™ 27-05CH Metallocene Polyethylene Resin (European Grade)
- ExxonMobil Santoprene® 691-65W175 Thermoplastic Vulcanizate
- Abatron AboCast 8708-9 One-Component Structural/Dielectric Epoxy
- Azoty Tarnow™ Tarnamid® T-27 GF20 FRV2 Polyamide 6 - Flame Retarded, Reinforced
- A. Schulman PP 3488-01 Polypropylene Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved