Styrolution PS 5400/5401 HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 5400/5401 HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good ESCRHigh ImpactLow gloss (matte finish)USP Class VI certifiedUL Classification 94 HBInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 50 | 50 | ASTM D 785 |
| Tensile Strength, Yield | 20.3 MPa | 2950 psi | ASTM D 638 |
| Elongation at Break | 55 % | 55 % | ASTM D 638 |
| Tensile Modulus | 1.86 GPa | 270 ksi | ASTM D 638 |
| Flexural Strength | 41.6 MPa | 6030 psi | ASTM D 790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D 638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D 696 |
| Vicat Softening Point | 100 °C @Load 1.02 kg |
212 °F @Load 2.25 lb |
120°C/h; ASTM D 1525 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 15 % | 15 % | Specular Gloss, 60°; ASTM D 523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.5 @Thickness 1.00 mm, Frequency 1.00e+6 Hz |
2.5 @Thickness 0.0394 in, Frequency 1.00e+6 Hz |
ASTM D 150 |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | ASTM D 696 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPC-30T UV EXT 1148 Polypropylene Copolymer (PP Copolymer)
- Lehmann & Voss LUVOCOM® 1114-0717 PAEK, with carbon fiber and PTFE
- Multibase Multi-Flex® A 5003 TPE Thermoplastic Elastomer
- Teknor Apex Monprene® MP-2156-L1 Thermoplastic Elastomer
- Teknor Apex Monprene® MP-2880E Thermoplastic Elastomer
- Lubrizol Stat-Rite® X-5065 Static Control IDP-TPU Elastomeric Polymer Alloy
- A. Schulman POLYBATCH™ White LL8575 AP Concentrate Based In LLDPE
- Fainplast Compounds GA 88/3 Flexible PVC, Flame Retardant Sheathing
- Akro-Plastic Akromid® A3 (2414) PA 6.6 Conditioned
Copyright © lookpolymers.com All Rights Reserved