Styrolution Terblend® N 3154 ASA / PA, 8% Mineral filled
| Category | Polymer , Thermoplastic , ASA Polymer , Nylon |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® N 3154 ASA / PA, 8% Mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terblend N 3154 is an 8% mineral filled ABS/PA blend with good dimensional stability and enhanced rigidity.High dimensional stabilityEnhanced rigidityMineral filled (8%)Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 3.9 % @Temperature 23.0 °C |
3.9 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| Elongation at Break | 35 % | 35 % | ISO 527 |
| Elongation at Yield | 2.9 % | 2.9 % | ISO 527 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ISO 75 |
| Vicat Softening Point | 105 °C @Load 5.10 kg |
221 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 130 °C @Load 1.02 kg |
266 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dissipation Factor | 0.015 @Frequency 100 Hz |
0.015 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 285 °C | 482 - 545 °F | ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | ISO 294 |
| Injection Velocity | 40.0 mm/sec | 1.57 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- PTS SAN-82TR SAN Resin
- PTS Tristar® PC-30GFR 30% Glass Reinforced Polycarbonate
- ICO Polymers ICOFLOâ„¢ 510-5051 800 Micron LDPE Powder
- SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC (Asia Pacific)
- Sumitomo Bakelite North America E 7459A Long Glass Fiber Reinforced Epoxy
- Chase Plastics CP Pryme® NN133GL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated
- DSM Stanyl® TW441 (COND) Nylon 46 High Viscosity, Heat Stabilized, Lubricated (North America)
- Asahi Kasei Thermylene® P7-30FG-0684 30% Glass Fiber Reinforced, Heat and UV Stabilized
- 3M Scotch-Weld™ PS67 Pipe Sealant Anaerobic Adhesives
Copyright © lookpolymers.com All Rights Reserved