Styrolution Terblend® N NG-04 20% Glass Filled ABS/PA6 (Conditioned)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced , Nylon |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® N NG-04 20% Glass Filled ABS/PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terblend N NG-04 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, low mold shrinkage and high heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | dry; ISO 1183 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Melt Flow | 11 g/10 min @Load 10.0 kg, Temperature 240 °C |
11 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 2 in/min; ASTM Test |
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 |
| 5.0 % | 5.0 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 3.59 GPa | 521 ksi | ASTM Test |
| 4.10 GPa | 595 ksi | 1mm/min; ISO 527 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+11 ohm-cm | >= 1.00e+11 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
IEC 60250 |
| 5.0 @Frequency 1.00e+6 Hz |
5.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dissipation Factor | 0.050 @Frequency 1.00e+6 Hz |
0.050 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 265 °C | 509 °F | Injection molding |
| Injection Velocity | 65.0 mm/sec | 2.56 in/sec | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Active America | |
| Primary Processing Technique | Injection Molding | |
| UL.UL-C | Yes |