| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 200-3 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 200-3 polycarbonate resin is produced in compliance with the US Food and Drugs Administration (FDA) and EU food contact regulation. This resin provides excellent impact resistance, heat distortion resistance and optical clarity as well as high melt strength for sheet extrusion applications. Available in natural color onlyMain Characteristics:US FDA 21 CFR 177.1580CSANSFUnderwriters Laboratory (UL)EU food contact 200/72/ECApplications:Small appliancesSheet and profile extrusionHousewaresInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/B; ASTM D792 |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4; ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 74 | 74 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
| 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | 3-point; ISO 178 |
| 96.5 MPa | 14000 psi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| Flexural Modulus | 2.41 GPa | 350 ksi | Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790 |
| Izod Impact, Notched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 93.0 kJ/m² @Temperature 23.0 °C |
44.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256; ISO 180 |
| Tensile Impact Strength | 630 kJ/m² | 300 ft-lb/in² | ASTM D1822 |
| Dart Drop, Total Energy | 93.8 J | 69.2 ft-lb | 3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Annealed; ISO 75-2/B; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Unannealed; ASTM D648; ISO 75-2/A |
| 143 °C | 289 °F | Annealed; ASTM D648; ISO 75-2/A | |
| Vicat Softening Point | 151 °C @Load 5.10 kg |
304 °F @Load 11.2 lb |
Rate A (50°C/h); ISO 306/B50; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 26 % | 26 % | ISO 4289-2 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542; ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| 17.0 kV/mm | 432 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 Hz |
0.0010 @Frequency 50.0 Hz |
ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Average Extent of Burring | 3 cm | ASTM D635 |