Styron CALIBREâ„¢ 302V-6 LD Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 302V-6 LD Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: CALIBREâ„¢ 302V-6 LD HC18010009 Polycarbonate is an opalescent white extrusion-grade resin containing a proprietary light diffusion package that offers an excellent combination of light transmission. Light diffusion and whiteness for electronic signage and lighting applications and has been specifically designed to be used with LED light sources. CLAIBRE 302V-6 LD HC18010009 is UV stabilized, has outstanding impact resistance, heat distortion resistance, and meets UL 94 V-2 ratingApplications:LED back-lit sign faces and channel lettersComplies with:CSA (Canadian Standards Association)UL (Underwriters Laboratory, Inc.)Information provided by Styron
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183/A; ASTM D792
Water Absorption 0.32 %

@Temperature 23.0 °C
0.32 %

@Temperature 73.4 °F
Equilibrium, 50% RH; ISO 62; ASTM D570
0.15 %

@Temperature 23.0 °C,
Time 86400 sec
0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62; ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 5.6 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.6 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.0 MPa
10400 psi
ISO 527-2/50
72.4 MPa
10500 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527-2/50; ASTM D638
Elongation at Break 130 %
130 %
50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ASTM D638
Tensile Modulus 2.31 GPa
335 ksi
50 mm/min; ISO 527-2/50; ASTM D638
Flexural Strength 91.0 MPa
13200 psi
3-point, 2.0 mm/min; ISO 178
91.7 MPa
13300 psi
Method I (3 point load), 2.0 mm/min; ASTM D790
Flexural Modulus 2.31 GPa
335 ksi
Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Izod Impact, Notched 9.60 J/cm

@Temperature 23.0 °C
18.0 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Izod Impact, Notched (ISO) 94.0 kJ/m²

@Temperature 23.0 °C
44.7 ft-lb/in²

@Temperature 73.4 °F
ISO 180/4A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D256; ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.0 µm/m-°C
37.8 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 126 °C
259 °F
Unannealed; ASTM D648
139 °C
282 °F
Annealed; ASTM D648
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
V-2

@Thickness 3.20 mm
V-2

@Thickness 0.126 in
Optical Properties Metric English Comments
Transmission, Visible 25 %

@Wavelength 4500 nm
25 %

@Wavelength 4500 nm
ASTM D1003
35 %

@Wavelength 3200 nm
35 %

@Wavelength 3200 nm
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 60.0 Hz
3.0

@Frequency 60.0 Hz
ASTM D150
3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 50.0 Hz
0.0010

@Frequency 50.0 Hz
ASTM D150
0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150