Styron CALIBREâ„¢ 701-10 Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 701-10 Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: CALIBREâ„¢ 701-10 resin is formulated and produced to supply clarity and enhanced ignition resistance. They do so while maintaining excellent physical properties and processability. CALIBRE 701-10 contains mold release.Main Characteristics:Underwriters Laboratory Inc. (UL)Applications:Industrial switchesCircuit breakersPlugs, sockets and switchesStreet lightsSafety lightsReflectorsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183/A
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ISO 294-4
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 66.0 MPa
9570 psi
ISO 527-2/50
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-2/50
Elongation at Break 120 %
120 %
ISO 527-2/50
Elongation at Yield 6.0 %
6.0 %
ISO 527-2/50
Tensile Modulus 2.30 GPa
334 ksi
ISO 527-2/50
Flexural Strength 100 MPa
14500 psi
2.0 mm/min (3 point); ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2.0 mm/min (3 point); ISO 178
Izod Impact, Notched (ISO) 88.0 kJ/m²

@Temperature 23.0 °C
41.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact, Notched 3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Hot Ball Pressure Test 123 °C
253 °F
IEC 60335-1
Deflection Temperature at 0.46 MPa (66 psi) 144 °C
291 °F
Annealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
Unannealed; ISO 75-2/A
140 °C
284 °F
Annealed; ISO 75-2/A
Vicat Softening Point 149 °C
300 °F
ISO 306/B50
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V

@Thickness 2.00 mm
250 V

@Thickness 0.0787 in
Solution A; IEC 60112