Styron CALIBREâ„¢ 891 20 Polycarbonate, General Purpose

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Styron
Trade Name CALIBRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 891 20 Polycarbonate, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CALIBRE® 890 series polycarbonate resins are a general purpose, superior ignition resistant grade equipped with a mold release package. The CALIBRE 890 series resins exhibit a high heat resistance, high impact and are rated V-0 at 1.6 mm, 5V at 3.2 mm according to UL-94(1).The CALIBRE 890 series resins are typically used in building and construction and in business equipment applications.Available Melt Flow Rates: 10, 20Associated products: CALIBRE 891: including a mold release package CALIBRE 893: including a mold release and UV stabilizer package.These numerical flame spread ratings are small scale test values and are not intended to reflect hazards presented by these or any other materials under actual fire conditions.Ignition resistant chemical additives increase resistance to burning from minor flame sources and permit properly manufactured end products to meet the requirements of certain flammability tests, but resins will burn rapidly under the right conditions of heat and oxygen feed.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM Data
Melt Density 1.13 g/cc
0.0408 lb/in³
Melt density
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Melt Flow 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM Data
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
Tensile Strength, Ultimate 58.6 MPa
8500 psi
ASTM Data
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO Data
Elongation at Break 115 %
115 %
ASTM Data
Elongation at Yield 6.0 %
6.0 %
ISO Data
Tensile Modulus 2.38 GPa
345 ksi
ASTM Data
Izod Impact, Notched 6.94 J/cm
13.0 ft-lb/in
ASTM Data
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
ISO Data, Low Temp
3.00 J/cm²
14.3 ft-lb/in²
ISO Data
Impact Test 62.2 J

@Temperature 23.0 °C
45.9 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.4 µm/m-°C

@Temperature 20.0 °C
38.0 µin/in-°F

@Temperature 68.0 °F
ASTM data
Specific Heat Capacity 2.10 J/g-°C
0.502 BTU/lb-°F
Thermal Conductivity 0.244 W/m-K
1.69 BTU-in/hr-ft²-°F
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
Unannealed; ASTM Data
Vicat Softening Point 151 °C
304 °F
Flammability, UL94 5VA

@Thickness 3.20 mm
5VA

@Thickness 0.126 in
UL94
Oxygen Index 36 %
36 %