Styron MAGNUMâ„¢ 357 HP Acrylonitrile Butadiene Styrene (ABS) Resin

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Styron
Trade Name Magnum™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron MAGNUMâ„¢ 357 HP Acrylonitrile Butadiene Styrene (ABS) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: MAGNUM™ ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes. Automotive MAGNUM ABS resins offer a wide range of gloss, viscosity, impact strength and heat properties for use in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.5 to 12 ft-lb/in and heat distortion temperatures from 165 to 190°F are available. Available primarily as natural plus concentrates, MAGNUM ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars, and exterior trim parts requiring painting and plating. MAGNUM 357 HP ABS resin is a medium gloss, high heat material that has slightly higher heat resistance and a little higher melt flow rate than MAGNUM 358 HP ABS resinInformation provided by Styron
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ASTM D792
Melt Density 1.08 g/cc
0.0390 lb/in³
Maximum Moisture Content 0.10
0.10
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 2.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 2.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 33.1 MPa
4800 psi
Type I, 51 mm/min; ASTM D638
Tensile Strength, Yield 37.9 MPa
5500 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 45 %
45 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 2.00 GPa
290 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 62.1 MPa
9010 psi
Type I, 1.3 mm/min; ASTM D790
Flexural Modulus 2.21 GPa
321 ksi
Type I, 1.3 mm/min; ASTM D790
Izod Impact, Notched 1.30 J/cm

@Thickness 3.20 mm,
Temperature -18.0 °C
 2.44 ft-lb/in

@Thickness 0.126 in,
Temperature -0.400 °F
 0.25 mm Notch Depth; ASTM D256
3.10 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 5.81 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 0.25 mm Notch Depth; ASTM D256
Dart Drop, Total Energy 22.6 J

@Thickness 3.20 mm,
Temperature -18.0 °C
 16.7 ft-lb

@Thickness 0.126 in,
Temperature -0.400 °F
 3.39 m/sec, Peak Energy; ASTM D3763
23.7 J

@Thickness 3.20 mm,
Temperature -18.0 °C
 17.5 ft-lb

@Thickness 0.126 in,
Temperature -0.400 °F
 3.39 m/sec, Total Energy; ASTM D3763
32.8 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 24.2 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 3.39 m/sec, Peak Energy; ASTM D3763
42.9 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 31.6 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 3.39 m/sec, Total Energy; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 81.0 µm/m-°C
45.0 µin/in-°F
ASTM D696
Thermal Conductivity 0.130 W/m-K
0.902 BTU-in/hr-ft²-°F
Melt; ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 104 °C

@Thickness 3.20 mm
 219 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.8 °C

@Thickness 3.20 mm
 190 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Vicat Softening Point 120 °C
248 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 260 - 282 °C
500 - 540 °F
Mold Temperature 37.8 - 82.2 °C
100 - 180 °F
Drying Temperature 82.2 - 85.0 °C
180 - 185 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Clamp Tonnage 2.8-4.1 kN/cm2
Ejection Temperature 127°C
No Flow Temperature 150°C
Screw Compression Ratio 1.5:1 to 3.5:1
Screw L/D Ratio 0.834027777777778