Styron Magnumâ„¢ 2620 ABS, Impact Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer Styron
Trade Name Magnum™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron Magnumâ„¢ 2620 ABS, Impact Grade.pdf
  Online Service   lookpolymers   27660005
Material Notes:
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming.The 2600 series of MAGNUM ABS resins are designated for use in healthcare applications. Both high and low gloss resins are available which have passed the USP XXIII Class IV medical testing. Other non-USP classified testing is also done on the MAGNUM 2600 series of ABS resins to evaluate the biocompatibility of the resins.MAGNUM 2620 ABS resin is a high gloss ABS with slightly higher impact strength over 2610 and has a slightly lower melt flow rate. MAGNUM 2620 represents the balance between flow and impact strength in the high gloss resins.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
Melt Flow 5.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
5.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell R 107
Tensile Strength, Ultimate 33.1 MPa
4800 psi
Tensile Strength, Yield 41.4 MPa
6000 psi
Elongation at Break 50 %
50 %
Elongation at Yield 2.5 %
2.5 %
ISO Data
Tensile Modulus 2.07 GPa
300 ksi
Izod Impact, Notched 2.94 J/cm
5.51 ft-lb/in
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
ISO Data, Low Temp
ISO Data
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO Data, Low Temp
2.40 J/cm²
11.4 ft-lb/in²
ISO Data
Impact Test 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 102 µm/m-°C

@Temperature 20.0 °C
56.7 µin/in-°F

@Temperature 68.0 °F
ISO data
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C
201 °F
Unannealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
Unannealed; 104°C (219°F) annealed; ASTM Data
Vicat Softening Point 108 °C
226 °F
Optical Properties Metric English Comments
Gloss 95 %
95 %
Gardner Gloss, 60°