Styron Magnumâ„¢ 345 ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Styron
Trade Name Magnum™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron Magnumâ„¢ 345 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming.MAGNUM ABS resins offer a wide range of processability and impact resistance for low gloss injection molding applications. Combined with heat resistance and tensile and flexural strength, MAGNUM ABS resins are used in a wide variety of injection molding applications.MAGNUM 345 ABS resin is the easiest processing low gloss, low impact strength injection molding resin. With a high melt flow rate of 12 g/10 min., it is often selected for hard to fill molds or long flow lengths.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM Data
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
Melt Flow 15 g/10 min

@Load 3.80 kg,
Temperature 230 °C
15 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM Data
Mechanical Properties Metric English Comments
Tensile Strength, Yield 37.9 MPa
5500 psi
ASTM Data
Elongation at Break 110 %
110 %
ASTM Data
Tensile Modulus 2.08 GPa
302 ksi
ASTM Data
Izod Impact, Notched 1.33 J/cm
2.49 ft-lb/in
ASTM Data
Impact Test 35.0 J

@Temperature 23.0 °C
25.8 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
Unannealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
Unannealed; ASTM Data
Vicat Softening Point 103 °C
217 °F
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in