Styron Magnumâ„¢ 9030 ABS, High Gloss

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Styron
Trade Name Magnum™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron Magnumâ„¢ 9030 ABS, High Gloss.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming.The MAGNUM 9000 series of high gloss ABS resins are designed to offer a wide range of impact strengths and melt flow rates to meet the needs of the durables injection molding markets. The 9000 series products offer typical Izod impact strength values from 210 to 400 J/m and melt flow rates ranging from 2.5 to 7.0 g/10min. The gloss values are typically greater than 95% on the 60. Gardner scale for the highest gloss resins and greater than 90% for those products having a broader range of gloss.MAGNUM 9030 ABS resin is one of the highest gloss resins combined with the highest impact strength and lowest melt flow rate in the 9000 series. MAGNUM 9030 is used primarily in injection molding applications like floor care equipment where this level of impact resistance is required.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM Data
Melt Density 0.911 g/cc
0.0329 lb/in³
Melt density
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
Melt Flow 2.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM Data
Mechanical Properties Metric English Comments
Hardness, Rockwell R 101
101
Tensile Strength, Ultimate 31.0 MPa
4500 psi
ASTM Data
Tensile Strength, Yield 37.2 MPa
5400 psi
ASTM Data
Elongation at Break 55 %
55 %
ASTM Data
Elongation at Yield 2.4 %
2.4 %
ISO Data
Tensile Modulus 1.93 GPa
280 ksi
ASTM Data
Izod Impact, Notched 4.00 J/cm
7.49 ft-lb/in
ASTM Data
Charpy Impact Unnotched NB
NB
ISO Data
NB
NB
ISO Data, Low Temp
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
ISO Data, Low Temp
3.20 J/cm²
15.2 ft-lb/in²
ISO Data
Impact Test 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature 20.0 °C
55.6 µin/in-°F

@Temperature 68.0 °F
ISO data
Specific Heat Capacity 1.96 J/g-°C
0.468 BTU/lb-°F
Thermal Conductivity 0.134 W/m-K
0.930 BTU-in/hr-ft²-°F
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Unannealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Unannealed; 100°C (212°F) annealed; ASTM Data
Vicat Softening Point 107 °C
225 °F
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in
Optical Properties Metric English Comments
Gloss 95 %
95 %
Gardner Gloss, 60°