Styron PulseÂ® 1550 ABS + Polycarbonate, 10% Glass Reinforced

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	Pulse®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron PulseÂ® 1550 ABS + Polycarbonate, 10% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PULSEÂ® 1550 Engineering resin is a 10% glass reinforced resin which offers a superior total performance with a balance of high heat resistance, practical toughness and ease of processing.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/inÂ³	ASTM Data
Melt Density	1.09 g/cc	0.0394 lb/inÂ³	Melt density
Water Absorption	0.15 %	0.15 %
Moisture Absorption at Equilibrium	0.32 %	0.32 %	Humidity Absorption
Linear Mold Shrinkage	0.0045 cm/cm	0.0045 in/in
Melt Flow	3.0 g/10 min @Load 3.80 kg, Temperature 230 Â°C	3.0 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM Data

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120
Tensile Strength, Ultimate	46.9 MPa	6800 psi	ASTM Data
Tensile Strength, Yield	53.8 MPa	7800 psi	ASTM Data
Elongation at Break	10 %	10 %	ASTM Data
Elongation at Yield	3.4 %	3.4 %	ISO Data
Tensile Modulus	3.80 GPa	551 ksi	ISO Data.
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM Data
	1.60 J/cm @Temperature -50.0 Â°C	3.00 ft-lb/in @Temperature -58.0 Â°F	ASTM Data
Charpy Impact Unnotched	5.00 J/cmÂ²	23.8 ft-lb/inÂ²	ISO Data, Low Temp
	9.00 J/cmÂ²	42.8 ft-lb/inÂ²	ISO Data
Charpy Impact, Notched	0.800 J/cmÂ²	3.81 ft-lb/inÂ²	ISO Data, Low Temp
	1.80 J/cmÂ²	8.57 ft-lb/inÂ²	ISO Data
Impact Test	17.0 J @Temperature -30.0 Â°C	12.5 ft-lb @Temperature -22.0 Â°F	Instrumented Dart Total Energy
	17.0 J @Temperature 23.0 Â°C	12.5 ft-lb @Temperature 73.4 Â°F	Instrumented Dart Total Energy

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	59.4 Âµm/m-Â°C @Temperature 20.0 Â°C	33.0 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM data
Specific Heat Capacity	2.10 J/g-Â°C	0.502 BTU/lb-Â°F
Thermal Conductivity	0.260 W/m-K	1.80 BTU-in/hr-ftÂ²-Â°F
Deflection Temperature at 1.8 MPa (264 psi)	127 Â°C	261 Â°F	Unannealed; 129Â°C (264Â°F) annealed; ASTM Data
Vicat Softening Point	144 Â°C	291 Â°F
Flammability, UL94	HB @Thickness 1.47 mm	HB @Thickness 0.0579 in