Sumitomo Bakelite North America RX® 865M Novolac Phenolic

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America RX® 865M Novolac Phenolic.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Fiberglass reinforced phenolic novolac compound featuring dimensional stability, moderate impact resistance, good strength and modulus.Information provided by Vyncolit, a Sumitomo Bak Group

Physical Properties	Metric	English	Comments
Bulk Density	0.650 g/cc	0.0235 lb/in³	Powder Density; ISO 60
Density	1.88 g/cc	0.0679 lb/in³	Relative Density; ISO 1183
Linear Mold Shrinkage	0.0010 cm/cm	0.0010 in/in	Compression Molding; ISO 2577

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell E	95	95	ISO 2039/2
Tensile Strength at Break	65.0 MPa	9430 psi	ISO 527
Flexural Strength	135 MPa	19600 psi	At Rupture; ISO 178
Flexural Modulus	20.0 GPa	2900 ksi	ISO 178
Compressive Strength	265 MPa	38400 psi	ISO 604
Izod Impact, Notched (ISO)	4.50 kJ/m²	2.14 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	17.0 µm/m-°C @Temperature 20.0 °C	9.44 µin/in-°F @Temperature 68.0 °F	ASTM E-831
CTE, linear, Transverse to Flow	39.0 µm/m-°C @Temperature 20.0 °C	21.7 µin/in-°F @Temperature 68.0 °F	ASTM E-831
Thermal Conductivity	0.740 W/m-K	5.14 BTU-in/hr-ft²-°F	ASTM C-518
Maximum Service Temperature, Air	150 °C	302 °F	UL 746B
Deflection Temperature at 1.8 MPa (264 psi)	>= 282 °C	>= 540 °F	Post Baked; ISO 75 A
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Dielectric Strength	13.5 kV/mm	343 kV/in	60Hz, Short Time, dry; ASTM D149
Arc Resistance	185 sec	185 sec	ASTM D495

Descriptive Properties	Value	Comments
Color	Black
Form	Flake
Main Filler	Glass Fiber
Molding Method	Compression, transfer, injection

Users viewing this material also viewed the following: