Sumitomo Bakelite North America SI 9002N-1 Silicone Compound
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America SI 9002N-1 Silicone Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Short fibergass reinforced silicone molding compound which offers moderate strength properties, dimensional stability, and excellent long-term thermal stability at elevated temperatures.Information provided by Vyncolit, a Sumitomo Bak Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.90 g/cc | 0.033 lb/in³ | Powder Density; ASTM D1895 |
| Density | 2.1 g/cc | 0.076 lb/in³ | Relative Density; ASTM D792 |
| Water Absorption | 0.3 % | 0.3 % | 48 hr @ 50°C; ASTM D570 |
| Linear Mold Shrinkage | 0.002 - 0.004 cm/cm | 0.002 - 0.004 in/in | Compression Molding; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ASTM D2583 |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
| Flexural Strength | 52.0 MPa | 7540 psi | At Rupture; ASTM D790 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ASTM D790 |
| Compressive Strength | 88.0 MPa | 12800 psi | ASTM D695 |
| Izod Impact, Notched | 0.220 J/cm | 0.412 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C @Temperature 20.0 °C |
18.3 µin/in-°F @Temperature 68.0 °F |
ASTM E-831 |
| Thermal Conductivity | 0.810 W/m-K | 5.62 BTU-in/hr-ft²-°F | ASTM C-518 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ASTM D648A |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.9 @Frequency 1e+6 Hz |
3.9 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| Dielectric Strength | 6.50 kV/mm | 165 kV/in | 60Hz, Step-by-Step, wet; ASTM D149 |
| 9.80 kV/mm | 249 kV/in | 60Hz, Short Time, wet; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| Arc Resistance | 200 sec | 200 sec | ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Gray, Red | |
| Form | Granular | |
| Main Filler | Glass Fiber | |
| Molding Method | Compression, transfer, injection |