TPI Porene® KU900 Super High Heat ABS

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer	Thai Petrochemical Industry Co. LTD.
Trade Name	Porene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TPI Porene® KU900 Super High Heat ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

INJECTION MOLDING. ELECTRICAL PARTS, AUTOMOTIVE APPLICATIONS, HOUSEHOLD GOODS, TOYSPorene® is a registered trademark of Thai Petrochemical Industry Co. LTD. Information provided by Dayson Polymers.

Physical Properties	Metric	English	Comments
Melt Flow	4.5 g/10 min @Load 10.0 kg, Temperature 220 °C	4.5 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	112	112	0.250 inch; ASTM D785
Tensile Strength at Break	49.0 MPa	7110 psi	ASTM D638
Flexural Yield Strength	70.3 MPa	10200 psi	ASTM D790
Flexural Modulus	2.35 GPa	341 ksi	ASTM D790
Izod Impact, Notched	1.28 J/cm	2.39 ft-lb/in	0.250 inches; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	114 °C	237 °F	0.250 inch; Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	104 °C	219 °F	Unannealed; 0.250 inches; ASTM D648
Flammability, UL94	HB	HB	0.126 inch

Processing Properties	Metric	English
Melt Temperature	220 - 260 °C	428 - 500 °F
Mold Temperature	40.0 - 80.0 °C	104 - 176 °F
Drying Temperature	90.0 - 100 °C	194 - 212 °F
Dry Time	2 - 3 hour	2 - 3 hour