TSE Industries EcoSPRAY® 350c Flame-Retardant Polyurethane Resin

Category Polymer , Thermoset , Polyurethane, TS
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries EcoSPRAY® 350c Flame-Retardant Polyurethane Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TSE-EcoSPRAY® 350c is an “Environmentally-Preferred Product” or EPP. It is a Thixotropic flame retardant polyurethane resin free of Styrene, and is an “ultra-low” emitting resin during application. TSE-EcoSPRAY® 350c is designed for spray-up applications requiring ANSI Z-124 approval. This PU resin has extensive ANSI Z-124 approvals and can be applied to reinforce both PU gel coat and thermoplastic substrates (i.e. Acrylic, Polycarbonate, ABS and co-extrusions thereof) in FRP plumbing fixture and spa shell applications.All information provided by TSE Industries
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
Part B
Viscosity 8000 cP
8000 cP
Part A
15000 cP
15000 cP
Part B
Mechanical Properties Metric English Comments
Hardness, Shore D 92 - 93
92 - 93
Clear Casting
92 - 93
92 - 93
20% Glass Laminate
92 - 93
92 - 93
21% Glass Spray-up Laminate
92 - 93
92 - 93
20% Glass RTM Laminate
Tensile Strength, Yield 50.0 - 52.0 MPa
7250 - 7540 psi
20% Glass Laminate
54.0 MPa
7830 psi
21% Glass Spray-up Laminate
60.0 MPa
8700 psi
Clear Casting
62.0 MPa
8990 psi
20% Glass RTM Laminate
Tensile Modulus 6.29 GPa
912 ksi
Clear Casting
7.72 GPa
1120 ksi
21% Glass Spray-up Laminate
7.72 - 7.93 GPa
1120 - 1150 ksi
20% Glass Laminate
8.41 GPa
1220 ksi
20% Glass RTM Laminate
Flexural Strength 82.0 MPa
11900 psi
Clear Casting
100 - 113 MPa
14500 - 16400 psi
20% Glass Laminate
121 MPa
17500 psi
21% Glass Spray-up Laminate
153 MPa
22200 psi
20% Glass RTM Laminate
Flexural Modulus 6.14 GPa
891 ksi
Clear Casting
6.00 - 6.30 GPa
870 - 914 ksi
20% Glass Laminate
7.10 GPa
1030 ksi
21% Glass Spray-up Laminate
8.83 GPa
1280 ksi
20% Glass RTM Laminate
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 233 °C
451 °F
20% Glass Laminate; unspecified load
233 °C
451 °F
21% Glass Spray-up Laminate
233 °C
451 °F
20% Glass RTM Laminate
Processing Properties Metric English Comments
Cure Time 25.0 min

@Temperature 57.2 - 62.8 °C
0.417 hour

@Temperature 135 - 145 °F
post-cure
Gel Time 3.00 - 18.0 min
3.00 - 18.0 min
when reacted at 1:1 by volume, based on the application
Shelf Life 6.00 Month

@Temperature 21.1 - 35.0 °C
6.00 Month

@Temperature 70.0 - 95.0 °F
Part B
6.00 Month

@Temperature 21.1 - 35.0 °C
6.00 Month

@Temperature 70.0 - 95.0 °F
Part A
Descriptive Properties Value Comments
Appearance Brown
Part A
Gray
Part B
Thixotropic Index 2.3
Part A
4.1
Part B