TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR Cumar P10 Plasticizer

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR Cumar P10 Plasticizer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Plasticizers should be used in all Millathane®76 compounds to better incorporate fillers and improve processing. Some plasticizers are not compatible with Millathane76, e.g. naphthenic and all paraffinic oils, however, a number of ester plasticizers perform very well.FormulationMillathane 76 100.0Zinc Stearate0.5N-550 Black40.0MBTS4.0MBT2.0Thanecure® ZM1.0Sulfur1.5Plasticizer10.0All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 62
62
80
80
heat aged 70 hours @ 100ºC
Tensile Strength, Yield 22.54 MPa
3269 psi
Elongation at Yield 621 %
621 %
100% Modulus 0.00230 GPa
0.334 ksi
200% Modulus 0.00489 GPa
0.709 ksi
300% Modulus 0.008301 GPa
1.204 ksi
Tear Strength 56.4 kN/m
322 pli
Die C
Compression Set 35.8 %

@Temperature 70.0 °C,
Time 79200 sec
35.8 %

@Temperature 158 °F,
Time 22.0 hour
Processing Properties Metric English Comments
Cure Time 7.00 min

@Temperature 155 °C
0.117 hour

@Temperature 311 °F
Descriptive Properties Value Comments
Weight Loss (%) 5
heat aged 70 hours @ 100ºC