TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer TSE Industries, Inc
Trade Name Millathane®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subjected to high wear in service. It has a unique combination of excellent properties, such as low temperature characteristics, and resistance to heat deterioration, ozone cracking, weathering and swelling in oils or solvents.Increasing the concentration of sulfur produces a faster rate and a higher state of cure — better abrasion resistance, better dynamic properties, and high hardness — equivalent compression set, and somewhat poorer aging properties. Decreasing the sulfur content results in a reduced state of cure.FormulationMillathane CM 100.0N330 Carbon Black30.0Coumarone-Indene Resin15.0MBTS4.0MBT1.0Zinc Stearate0.75CAYTUR 40.35Sulfur0.75All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 65
65
68
68
after 7 days at 100ºC
Tensile Strength, Yield 27.9 MPa
4050 psi
after 7 days at 100ºC
31.0 MPa
4500 psi
Elongation at Break 390 %
390 %
after 7 days at 100ºC
480 %
480 %
300% Modulus 0.01465 GPa
2.125 ksi
0.01948 GPa
2.825 ksi
after 7 days at 100ºC
Abrasion 335
335
NBS Index
Compression Set 19 %

@Temperature 70.0 °C,
Time 79200 sec
19 %

@Temperature 158 °F,
Time 22.0 hour
Method B
Processing Properties Metric English Comments
Cure Time 60.0 min

@Temperature 142 °C
1.00 hour

@Temperature 287 °F
Descriptive Properties Value Comments
?T, Platen (ºC) 60
Heat Build-up, Internal Temp (ºC) 135
Goodrich Flexometer