TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.25 PHR Zinc Stearate

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer TSE Industries, Inc
Trade Name Millathane®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.25 PHR Zinc Stearate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear strength, oil and fuel resistance, and ozone resistance. The life expectancy of urethane is often 5 times longer than other elastomers, thus saving material costs and downtime expense. One shortcoming of polyurethanes is loss of physical properties at temperatures over 180°F (82°C). MILLATHANE HT has overcome this weakness.Zinc stearate, when used as a co-activator with THANECURE® ZM, permits shorter cure times with improved compression set properties. Zinc stearate does contribute some lubricity to the batch and helps prevent sticking to mill rolls and surfaces of internal mixers, however its primary use is to help activate the cure and produce a tighter cure.All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 83
83
Tensile Strength, Yield 18.07 MPa
2621 psi
Elongation at Yield 395 %
395 %
100% Modulus 0.00574 GPa
0.833 ksi
200% Modulus 0.01176 GPa
1.706 ksi
300% Modulus 0.01610 GPa
2.335 ksi
Tear Strength 40.0 kN/m
228 pli
Die C
Compression Set 59 %

@Temperature 70.0 °C,
Time 79200 sec
59 %

@Temperature 158 °F,
Time 22.0 hour
Processing Properties Metric English Comments
Cure Time 12.0 min

@Temperature 160 °C
0.200 hour

@Temperature 320 °F
Press cured
Descriptive Properties Value Comments
DIN Abrasion (mm³) 124