Techmer ES ElastoblendÂ® PA6 IM 7050

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized , Nylon 6, Impact Grade , Nylon 6, Nucleated
Manufacturer	Techmer ES
Trade Name	Elastoblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES ElastoblendÂ® PA6 IM 7050.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier, Nucleating Agent and LubricantFeatures: Heat Stabilized, Impact Modified, Nucleated and LubricatedInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/inÂ³	ASTM D792
Water Absorption	1.5 % @Time 86400 sec	1.5 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.014 cm/cm @Thickness 3.17 mm	0.014 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	109	109	ASTM D785
Tensile Strength, Yield	55.2 MPa	8000 psi	ASTM D638
Elongation at Break	60 %	60 %	ASTM D638
Flexural Strength	78.6 MPa	11400 psi	ASTM D790
Flexural Modulus	1.93 GPa	280 ksi	ASTM D790
Izod Impact, Notched	3.20 J/cm @Thickness 3.17 mm, Temperature -40.0 Â°C	6.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 Â°F	ASTM D256
	4.27 J/cm @Thickness 3.17 mm, Temperature 22.8 Â°C	8.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 Â°F	ASTM D256
	4.54 J/cm @Thickness 3.17 mm, Temperature -20.0 Â°C	8.50 ft-lb/in @Thickness 0.125 in, Temperature -4.00 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	95.4 Âµm/m-Â°C	53.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	171 Â°C	340 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	61.1 Â°C	142 Â°F	Unannealed; ASTM D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Dielectric Strength	18.1 kV/mm	460 kV/in	Method A (Short-Time); ASTM D149