Techmer ES Elastoblend® PA6/6 GF17 IM2 L 17% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6/6 GF17 IM2 L 17% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 17% Filler by WeightAdditive: Lubricant and Impact ModifierFeatures: Lubricant and Impact ModifiedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.17 mm |
0.0090 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.71 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.20 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C | 44.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs NA1040 Na2S2O3 ·3H2O Sodium thiosulfate pentahydrate
- PolyOne Geon™ Vinyl Flexible A4DU5 Polyvinyl Chloride, Flexible (PVC, Flexible)
- MetalTek MTEK 175 Cast UNS C95400 Aluminum Bronze
- SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific)
- Styron CALIBREâ„¢ 340 TNIR Polycarbonate Resin
- Sax Polymers SAXATEC 6120 AES
- DuPont Performance Polymers Zytel® 73G50HSLA BK416 Nylon 6 (Unverified Data**)
- DSM Akulon® F232-DH Nylon 6 (European Grade) (Dry) (discontinued **)
- Henkel Hysol EA 9394 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved