Techmer ES HiFill® PA6 GF30 L 30% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6 GF30 L 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: LubricantFeatures: LubricatedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 | |
| Water Absorption | 0.85 % @Time 86400 sec |
0.85 % @Time 24.0 hour |
ASTM D570 |
| 1.3 % @Time 86400 sec |
1.3 % @Time 24.0 hour |
ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| 121 | 121 | ASTM D785 | |
| Tensile Strength, Yield | 162 MPa | 23500 psi | ASTM D638 |
| 176 MPa | 25500 psi | ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 3.0 % | 3.0 % | ASTM D638 | |
| Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
| 276 MPa | 40000 psi | ASTM D790 | |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D790 |
| 8.96 GPa | 1300 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 11.2 J/cm @Thickness 3.17 mm |
21.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.4 µm/m-°C | 8.00 µin/in-°F | ASTM D696 |
| 16.2 µm/m-°C | 9.00 µin/in-°F | ASTM D696 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| 218 °C | 425 °F | Unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | Method A (Short-Time); ASTM D149 |