Techmer ES Luriblend® PA4/6 CF30 TL10 30% Carbon Filled

Category Polymer , Thermoplastic , Nylon , Nylon 46
Manufacturer Techmer ES
Trade Name Luriblend®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Techmer ES Luriblend® PA4/6 CF30 TL10 30% Carbon Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(10%)Features: LubricatedTPCI# 8661150Information provided by TP Composites, Inc.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ASTM D792
Water Absorption 2.0 %

@Time 86400 sec
2.0 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 193 MPa
28000 psi
ASTM D638
Elongation at Break 2.6 %
2.6 %
ASTM D638
Flexural Strength 290 MPa
42000 psi
ASTM D790
Flexural Modulus 17.9 GPa
2600 ksi
ASTM D790
Izod Impact, Notched 0.747 J/cm

@Thickness 3.17 mm
1.40 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.0 µm/m-°C
15.0 µin/in-°F
ASTM D696
Melting Point 295 °C
563 °F
Deflection Temperature at 0.46 MPa (66 psi) 293 °C
560 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 285 °C
545 °F
Unannealed; ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 10 ohm-cm
10 ohm-cm
ASTM D257