Teijin Multilon T-2711 Standard, Automobile Part Series PC/ABS Polymer Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Teijin
Trade Name Multilon
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Multilon T-2711 Standard, Automobile Part Series PC/ABS Polymer Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC/ABS polymer alloy general grade developed for automobile parts use. It has high heat resistance, impact strength, light resistance and fluidity, particularly, the high impact strength in a wide range from -30 to over 100. Therefore, it is getting good estimation in a plurality of applications as automobile parts. Higher fluidity and thermal stability enable various processings such as, a gas-assist molding, hot-runner molding and compression molding.Applications:Car interior components (cluster, panels etc.)Audio and car-navigation equipment parts etc.Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
50mm/min; ISO 527
Tensile Strength, Yield 56.0 MPa
8120 psi
50mm/min; ISO 527
Elongation at Break 110 %
110 %
50mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
50mm/min; ISO 527
Tensile Modulus 2.25 GPa
326 ksi
1mm/min; ISO 527
Flexural Strength 85.0 MPa
12300 psi
2mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
2mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 8.00 J/cm²
38.1 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 20.0 °C
44.4 µin/in-°F

@Temperature 68.0 °F
ISO 11359
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 20.0 °C
44.4 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 124 °C
255 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
219 °F
ISO 75
Vicat Softening Point 122 °C
252 °F
50°C/hr, 50N; ISO 306
Electrical Properties Metric English Comments
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093