Teijin Panlite® BN-8120R Improved Mold Release, Carbon Fiber Reinforced, Flame Resistant Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced
Manufacturer Teijin
Trade Name Panlite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® BN-8120R Improved Mold Release, Carbon Fiber Reinforced, Flame Resistant Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CF 20% reinforced grade, meeting UL 94 V-2. It has excellent strength, stiffness, heat resistance and electric conductivity. Other features are flame retardance, low molding shrinkage and dimensional accuracy.Applications:Mechanical, electric and electronic components that need stiffness and strengthMechanical, electric and electronic components that need extremely high dimensional accuracy.Mechanical, electric and electronic components that need electric conductivity or antistatic propertyInformation provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.14 %
0.14 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.00020 - 0.0020 cm/cm

@Thickness 4.00 mm
0.00020 - 0.0020 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Thickness 4.00 mm
0.0030 - 0.0050 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
50mm/min; ISO 527
Elongation at Break 1.5 %
1.5 %
50mm/min; ISO 527
Tensile Modulus 13.0 GPa
1890 ksi
1mm/min; ISO 527
Flexural Strength 185 MPa
26800 psi
2mm/min; ISO 178
Flexural Modulus 11.5 GPa
1670 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 2.30 J/cm²
10.9 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature 20.0 °C
11.1 µin/in-°F

@Temperature 68.0 °F
ISO 11359
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 147 °C
297 °F
ISO 75
Vicat Softening Point 151 °C
304 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical with Impact 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity 0.10 - 10 ohm-cm
0.10 - 10 ohm-cm
IEC 60093
Surface Resistance 1.0 - 100 ohm
1.0 - 100 ohm
IEC 60093