Teijin Panlite® BS-8110R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced
Manufacturer Teijin
Trade Name Panlite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® BS-8110R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CF 10% reinforced grade, meeting UL 94 V-2. it is compounded with fluorine powder to improve friction and abrasion resistance and also exhibits a mold release property, maintaining excellent characteristics of polycarbonate resinApplications:Mechanical, electric and electronic components that need abrasion and friction resistance.Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Water Absorption 0.16 %
0.16 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 4.00 mm
0.0010 - 0.0030 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 4.00 mm
0.0040 - 0.0060 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
50mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
50mm/min; ISO 527
Tensile Modulus 7.80 GPa
1130 ksi
1mm/min; ISO 527
Flexural Strength 160 MPa
23200 psi
2mm/min; ISO 178
Flexural Modulus 7.50 GPa
1090 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 2.70 J/cm²
12.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 30.0 µm/m-°C

@Temperature 20.0 °C
16.7 µin/in-°F

@Temperature 68.0 °F
ISO 11359
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 147 °C
297 °F
ISO 75
Vicat Softening Point 152 °C
306 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical with Impact 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity 1.0 - 100 ohm-cm
1.0 - 100 ohm-cm
IEC 60093
Surface Resistance 10 - 1000 ohm
10 - 1000 ohm
IEC 60093