Teijin Panlite® G-3410H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled
Manufacturer	Teijin
Trade Name	Panlite®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Teijin Panlite® G-3410H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Reinforced with 10 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPrecision machinery components that need dimensional accuracy.Components that need paint finishInformation provided by Teijin Chemicals Ltd.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/in³	ISO 1183
Water Absorption	0.16 %	0.16 %	in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage	0.0030 - 0.0050 cm/cm @Thickness 4.00 mm	0.0030 - 0.0050 in/in @Thickness 0.157 in
Linear Mold Shrinkage, Transverse	0.0040 - 0.0060 cm/cm @Thickness 4.00 mm	0.0040 - 0.0060 in/in @Thickness 0.157 in

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	70.0 MPa	10200 psi	50mm/min; ISO 527
Elongation at Break	4.0 %	4.0 %	50mm/min; ISO 527
Tensile Modulus	3.30 GPa	479 ksi	1mm/min; ISO 527
Flexural Strength	115 MPa	16700 psi	2mm/min; ISO 178
Flexural Modulus	3.40 GPa	493 ksi	2mm/min; ISO 178
Charpy Impact Unnotched	7.00 J/cm²	33.3 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	50.0 µm/m-°C @Temperature 20.0 °C	27.8 µin/in-°F @Temperature 68.0 °F	ISO 11359
CTE, linear, Transverse to Flow	60.0 µm/m-°C @Temperature 20.0 °C	33.3 µin/in-°F @Temperature 68.0 °F	ISO 11359
Deflection Temperature at 0.46 MPa (66 psi)	142 °C	288 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	135 °C	275 °F	ISO 75
Vicat Softening Point	145 °C	293 °F	50°C/hr, 50N; ISO 306
UL RTI, Electrical	130 °C @Thickness 1.47 mm	266 °F @Thickness 0.0579 in	UL 746B
UL RTI, Mechanical with Impact	120 °C @Thickness 1.47 mm	248 °F @Thickness 0.0579 in	UL 746B
UL RTI, Mechanical without Impact	130 °C @Thickness 1.47 mm	266 °F @Thickness 0.0579 in	UL 746B
Flammability, UL94	HB @Thickness 0.430 mm	HB @Thickness 0.0169 in
	V-2 @Thickness 0.800 mm	V-2 @Thickness 0.0315 in
	V-1 @Thickness 3.00 mm	V-1 @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.2 @Frequency 100 Hz	3.2 @Frequency 100 Hz	IEC 60250
	3.2 @Frequency 1e+6 Hz	3.2 @Frequency 1e+6 Hz	IEC 60250
Dielectric Strength	35.0 kV/mm	889 kV/in	IEC 60243
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz	IEC 60250
	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	175 V	175 V	IEC 60112