Teijin Panlite® G-3430H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Teijin |
| Trade Name | Panlite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Panlite® G-3430H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with 30 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPrecision machinery components that need dimensional accuracy.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.12 % | 0.12 % | in water, 23°C, 24h; ISO 62 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | 50mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 6.70 GPa | 972 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 155 MPa | 22500 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 6.60 GPa | 957 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | ISO 75 |
| Vicat Softening Point | 146 °C | 295 °F | 50°C/hr, 50N; ISO 306 |
| UL RTI, Electrical | 130 °C @Thickness 1.47 mm |
266 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical with Impact | 125 °C @Thickness 1.47 mm |
257 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical without Impact | 130 °C @Thickness 1.47 mm |
266 °F @Thickness 0.0579 in |
UL 746B |
| Flammability, UL94 | HB @Thickness 0.430 mm |
HB @Thickness 0.0169 in |
|
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
||
| V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 60250 |
| 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |