Teknor Apex APEX® 92-A2292C-90 Polyvinyl Chloride, Flexible

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Flexible Grade , PVC, Wire and Cable Grade
Manufacturer Teknor Apex Company
Trade Name APEX®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex APEX® 92-A2292C-90 Polyvinyl Chloride, Flexible.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Notes: 105°C General Purpose; RoHS Compliant Features: Flame Retardant; High Heat Resistance Uses: Cable JacketingForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molded ComponentsInformation Provided by Teknor Apex
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 90
90
15 seconds; ASTM D2240
Tensile Strength at Break 17.9 MPa
2600 psi
ASTM D638
Elongation at Break 290 %
290 %
ASTM D638
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
Continuous Use; ASTM D794
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
ALL
V-1

@Thickness 2.40 mm
V-1

@Thickness 0.0945 in
ALL
V-0

@Thickness 2.40 mm
V-0

@Thickness 0.0945 in
BK
V-0

@Thickness 2.40 mm
V-0

@Thickness 0.0945 in
RD
Oxygen Index 27 %
27 %
ASTM D2863
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V

@Thickness 2.40 mm
>= 600 V

@Thickness 0.0945 in
UL 746
Hot Wire Ignition, HWI 60 - 120 sec

@Thickness 1.50 mm
60 - 120 sec

@Thickness 0.0591 in
UL 746
60 - 120 sec

@Thickness 2.40 mm
60 - 120 sec

@Thickness 0.0945 in
UL 746
High Amp Arc Ignition, HAI <= 120 arcs

@Thickness 1.50 mm
<= 120 arcs

@Thickness 0.0591 in
UL 746
<= 120 arcs

@Thickness 2.40 mm
<= 120 arcs

@Thickness 0.0945 in
UL 746
Descriptive Properties Value Comments
Appearance Opaque