ThyssenKrupp XABO® 960 Structural Steel

Category	Metal , Ferrous Metal , Carbon Steel , Low Carbon Steel
Manufacturer	ThyssenKrupp
Trade Name	XABO®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ThyssenKrupp XABO® 960 Structural Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This Material Specification applies to liquid-quenched and tempered heavy plates from 3 up to 100 mm in thickness, made of the high-strength special structural steels XABO® 890 and XABO® 960.Application: The steels are used for welded constructions of all kinds such as transport vehicles, mobile cranes, hoistings and mining equipment, pressure vessels and penstocks.Information Provided by Thyssen Krupp

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	900 - 1050 MPa	131000 - 152000 psi	80<x=100mm
	920 - 1070 MPa	133000 - 155000 psi	60<x=80mm
	970 - 1100 MPa	141000 - 160000 psi	50<x=60mm
	980 - 1150 MPa @Thickness 50.0 mm	142000 - 167000 psi @Thickness 1.97 in
Tensile Strength, Yield	>= 850 MPa	>= 123000 psi	80<x=100mm
	>= 870 MPa	>= 126000 psi	60<x=80mm
	>= 920 MPa	>= 133000 psi	50<x=60mm
	>= 960 MPa @Thickness 50.0 mm	>= 139000 psi @Thickness 1.97 in
Elongation at Break	>= 10 %	>= 10 %
Charpy Impact	27.0 J @Temperature -40.0 °C	19.9 ft-lb @Temperature -40.0 °F	Transverse
	30.0 J @Temperature -20.0 °C	22.1 ft-lb @Temperature -4.00 °F	Transverse
	30.0 J @Temperature -40.0 °C	22.1 ft-lb @Temperature -40.0 °F	Longitudinal
	35.0 J @Temperature 0.000 °C	25.8 ft-lb @Temperature 32.0 °F	Transverse
	40.0 J @Temperature -20.0 °C	29.5 ft-lb @Temperature -4.00 °F	Longitudinal
	50.0 J @Temperature 0.000 °C	36.9 ft-lb @Temperature 32.0 °F	Longitudinal

Component Elements Properties	Metric	English
Aluminum, Al	<= 0.80 %	<= 0.80 %
Carbon, C	<= 0.18 %	<= 0.18 %
Chromium, Cr	<= 0.80 %	<= 0.80 %
Manganese, Mn	<= 1.6 %	<= 1.6 %
Molybdenum, Mo	<= 0.70 %	<= 0.70 %
Nickel, Ni	<= 2.0 %	<= 2.0 %
Phosphorous, P	<= 0.020 %	<= 0.020 %
Silicon, Si	<= 0.50 %	<= 0.50 %
Sulfur, S	<= 0.010 %	<= 0.010 %
Vanadium, V	<= 0.10 %	<= 0.10 %