Tipco Tipcofil® AG 800 - 40% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Tipco Industries Ltd., India
Trade Name Tipcofil®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tipco Tipcofil® AG 800 - 40% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ASTM D792
Water Absorption 1.0 %
1.0 %
ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Melt Flow 5.0 g/10 min
5.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 180 MPa
26100 psi
ASTM D638
Elongation at Break >= 4.0 %
>= 4.0 %
ASTM D638
Flexural Yield Strength 225 MPa
32600 psi
ASTM D790
Flexural Modulus 9.40 GPa
1360 ksi
ASTM D790
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ASTM D648
Vicat Softening Point 218 °C
424 °F
ASTM D1525
Processing Properties Metric English Comments
Processing Temperature 270 °C
518 °F
Rear Barrel Temperature 250 °C
482 °F
Middle Barrel Temperature 260 °C
500 °F
Front Barrel Temperature 270 °C
518 °F
Nozzle Temperature 265 °C
509 °F
Mold Temperature 105 °C
221 °F
Drying Temperature 85.0 °C
185 °F