Tisan TISESTER® 15% Glass Fiber Reinforced and Heat Stabilized Polybutylene Terephthalate

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Tisan Engineering Plastics
Trade Name TISESTER®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tisan TISESTER® 15% Glass Fiber Reinforced and Heat Stabilized Polybutylene Terephthalate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resistanceExcellent toughnessHigh temperature resistanceExcellent chemical resistanceElectrical isolation and arc resistanceHigh performanceEasy processabilityFast cycle time Glass fiber reinforcement imparts high shrinkage resistance and impact resistance to TISESTER products, yielding improvements in thermal features as well. PBT is resistant against solvents, exhibits low shrinkage during shaping, and it is mechanically strong, heat resistant for temperatures up to 150°C, and can be reinforced for flame retardance. Tisester compounds display sufficient resistance against hydrocarbons, alcohols, ethers, acids, and alkali solvents.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Ash 15 %
15 %
ISO 3451
Mechanical Properties Metric English Comments
Hardness, Shore A 82
82
ISO 868
Tensile Strength at Break 115 MPa
16700 psi
ISO 527-2
Tensile Strength, Yield 110 MPa
16000 psi
ISO 527-2
Elongation at Break 3.7 %
3.7 %
ISO 527-2
Elongation at Yield 3.5 %
3.5 %
ISO 527-2
Modulus of Elasticity 4.50 GPa
653 ksi
ISO 527-2
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 225 - 230 °C
437 - 446 °F
Vicat Softening Point 214 °C
417 °F
ISO 306
Heat Distortion Temperature 216 °C
421 °F
ISO 75-2
Flammability, UL94 HB
HB
Glow Wire Test 750 °C
1380 °F
60695-2-10
Electrical Properties Metric English Comments
Comparative Tracking Index 400 V
400 V
TS EN 60112
Processing Properties Metric English Comments
Feed Temperature 70.0 °C
158 °F
Rear Barrel Temperature 220 - 250 °C
428 - 482 °F
Aft-1. Region Temperature
Middle Barrel Temperature 220 - 250 °C
428 - 482 °F
Mid-2. Region Temperature
Front Barrel Temperature 220 - 250 °C
428 - 482 °F
Pre-3. Region Temperature
Nozzle Temperature 225 °C
437 °F
Melt Temperature 220 - 230 °C
428 - 446 °F
Drying Temperature 110 - 120 °C
230 - 248 °F
Predrying Temperature
Dry Time 4 - 5 hour
4 - 5 hour
Predrying Time
Moisture Content 0.30 %
0.30 %
ISO 62
Descriptive Properties Value Comments
Block Temperature 80°C