- Tisan TISLAMID® 66 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 66
Tisan TISLAMID® 66 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Tisan Engineering Plastics |
| Trade Name | TISLAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tisan TISLAMID® 66 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElectric isolationEasy processabilityHigh mechanical resistanceExcellent flame retardanceHigh moisture absorptionExcellent temperature resistanceHigh performance / affordable priceAbrasion resistanceTISLAMID has an excellent resistance to weak alkalis and organic solvents. It has a good resistance to weak acids, alcohols, hydrocarbons, and engine fuels. It has a medium resistance to strong alkalis and a weak resistance to strong acids.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |
| Ash | 15 % | 15 % | ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | ISO 527-2 |
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527-2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-2 |
| Elongation at Yield | 4.1 % | 4.1 % | ISO 527-2 |
| Modulus of Elasticity | 3.50 GPa | 508 ksi | ISO 527-2 |
| Izod Impact, Notched (ISO) | 3.60 kJ/m² | 1.71 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | |
| Vicat Softening Point | 245 °C | 473 °F | ISO 306 |
| Heat Distortion Temperature | 240 °C | 464 °F | ISO 75-2 |
| Flammability, UL94 | V-0 | V-0 | |
| Glow Wire Test | 960 °C | 1760 °F | 60695-2-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 325 V | 325 V | TS EN 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Aft-1. Region Temperature |
| Middle Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Mid-2. Region Temperature |
| Front Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Pre-3. Region Temperature |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | Predrying Temperature |
| Dry Time | 3 - 4 hour | 3 - 4 hour | Predrying Time |
| Moisture Content | 2.2 % | 2.2 % | ISO 62 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Block Temperature | 75-85°C |