Tisan TISLAMID® 66 30% Glass Filled Impact Modified, Heat Stabilized Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade
Manufacturer Tisan Engineering Plastics
Trade Name TISLAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tisan TISLAMID® 66 30% Glass Filled Impact Modified, Heat Stabilized Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElectric isolationEasy processabilityHigh mechanical resistanceExcellent flame retardanceHigh moisture absorptionExcellent temperature resistanceHigh performance / affordable priceAbrasion resistanceTISLAMID has an excellent resistance to weak alkalis and organic solvents. It has a good resistance to weak acids, alcohols, hydrocarbons, and engine fuels. It has a medium resistance to strong alkalis and a weak resistance to strong acids.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
Ash 30 %
30 %
ISO 3451
Mechanical Properties Metric English Comments
Tensile Strength at Break 118 MPa
17100 psi
ISO 527-2
Tensile Strength, Yield 120 MPa
17400 psi
ISO 527-2
Elongation at Break 3.3 %
3.3 %
ISO 527-2
Elongation at Yield 3.2 %
3.2 %
ISO 527-2
Modulus of Elasticity 6.50 GPa
943 ksi
ISO 527-2
Izod Impact, Notched (ISO) 19.0 kJ/m²
9.04 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 255 - 260 °C
491 - 500 °F
Vicat Softening Point 245 °C
473 °F
ISO 306
Heat Distortion Temperature 240 °C
464 °F
ISO 75-2
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
60695-2-10
Electrical Properties Metric English Comments
Comparative Tracking Index 500 V
500 V
TS EN 60112
Processing Properties Metric English Comments
Feed Temperature 70.0 - 90.0 °C
158 - 194 °F
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Aft-1. Region Temperature
Middle Barrel Temperature 260 - 280 °C
500 - 536 °F
Mid-2. Region Temperature
Front Barrel Temperature 260 - 280 °C
500 - 536 °F
Pre-3. Region Temperature
Nozzle Temperature 250 - 270 °C
482 - 518 °F
Melt Temperature 260 - 290 °C
500 - 554 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Predrying Temperature
Dry Time 3 - 4 hour
3 - 4 hour
Predrying Time
Moisture Content 1.6 %
1.6 %
ISO 62
Descriptive Properties Value Comments
Block Temperature 75-85°C
Copyright © lookpolymers.com All Rights Reserved