Topas Advanced Polymers TOPAS® 6015S-04 Cyclic Olefin Copolymer (COC)

Category Polymer , Thermoplastic , Cyclo Olefin Polymer
Manufacturer Topas Advanced Polymers
Trade Name TOPAS®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Topas Advanced Polymers TOPAS® 6015S-04 Cyclic Olefin Copolymer (COC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TOPAS® 6015S-04 is a general purpose injection molding grade. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for optics, healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve food and drug stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high (150°C) heat distortion temperature to withstand 121°C and 134°C steam sterilization protocols, as well as gamma and EtO procedures. Key applications and attributes: Drug delivery: Low leachables & extractables, low water transmission Prefilled syringes, vials, cartridges: Non-ionic, does not promote adsorption like glass Bottles: Minimally reactive, EtO/gamma/steam sterilizable Surgical instruments: Chemically resistant to alcohol, acetone, and acrylates IV containers and components: Transparent, withstands EtO/gamma/steam sterilization Labware: Temperature resistance, clarity and purity Optics: Clarity, low birefringence, low moisture sensitivity Electronics: Low dielectric constant, thermoplastic Food packaging: Not manufactured with BPA, phthalates, or halogens Healthcare and food: Broad regulatory approval Information provided by TOPAS Advanced Polymers
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Water Absorption at Saturation 0.010 %

@Temperature 23.0 °C
0.010 %

@Temperature 73.4 °F
ISO 62
Melt Flow 3.68 g/10 min

@Load 2.16 kg,
Temperature 260 °C
3.68 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
5mm/min; ISO 527-2/1A
Elongation at Yield 2.5 %
2.5 %
5mm/min; ISO 527-2/1A
Tensile Modulus 3.00 GPa
435 ksi
1mm/min; ISO 527-2/1A
Charpy Impact Unnotched 1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.160 J/cm²

@Temperature 23.0 °C
0.761 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75-1,-2
Vicat Softening Point 156 °C
313 °F
B50 (50°C/h 50N); ISO 306
Glass Transition Temp, Tg 158 °C
316 °F
10°C/min; ISO 11357-1,-2,-3
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Optical Properties Metric English Comments
Refractive Index 1.53
1.53
ISO 489
Transmission, Visible 91 %
91 %
ISO 13468-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Dielectric Constant 2.3

@Frequency 1.00e+9 Hz
2.3

@Frequency 1.00e+9 Hz
IEC 60250
2.35

@Frequency 1000 - 10000 Hz
2.35

@Frequency 1000 - 10000 Hz
IEC 60250
Dissipation Factor 0.000070

@Frequency 1.00e+9 Hz
0.000070

@Frequency 1.00e+9 Hz
IEC 60250
Comparative Tracking Index >= 600 V
>= 600 V
IEC 60112
Processing Properties Metric English Comments
Feed Temperature <= 110 °C
<= 230 °F
Nozzle Temperature 250 - 310 °C
482 - 590 °F
Zone 1 240 - 270 °C
464 - 518 °F
Zone 2 250 - 290 °C
482 - 554 °F
Zone 3 260 - 310 °C
500 - 590 °F
Zone 4 260 - 310 °C
500 - 590 °F
Mold Temperature 110 - 145 °C
230 - 293 °F
Injection Velocity 50.0 - 150 mm/sec
1.97 - 5.91 in/sec
Moderate to Fast
Injection Pressure 50.0 - 110 MPa
7250 - 16000 psi
Specific
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Specific
Back Pressure <= 15.0 MPa
<= 2180 psi
Specific
Screw Speed 50 - 200 rpm
50 - 200 rpm