Topas Advanced Polymers TOPAS® 8007X10 Cyclic Olefin Copolymer (COC)

Category Polymer , Thermoplastic , Cyclo Olefin Polymer
Manufacturer Topas Advanced Polymers
Trade Name TOPAS®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Topas Advanced Polymers TOPAS® 8007X10 Cyclic Olefin Copolymer (COC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TOPAS® 8007X10 is a highly UV-transparent version of our 8007 series of injection molding resins. Like the rest of the 8007 grades, 8007X10 is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for diagnostic and analytical products. It transmits ultraviolet light at lower wavelengths than other polymers. Analytical results are more accurate with pure TOPAS COC and its higher UV transmission for more precise analysis in contact with sensitive chemistries.Key applications and attributes:Cuvettes: UV transparency at low wavelengths Microplates and biochips: Dimensional stability and purity and chemical resistance Microfluidics: UV transmission; exceptional mold detail replicationOptics: Clarity, low birefringence, low fluorescence High purity applications: Not manufactured with BPA, phthalates, or halogens Information provided by TOPAS Advanced Polymers
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Water Absorption at Saturation 0.010 %

@Temperature 23.0 °C
0.010 %

@Temperature 73.4 °F
ISO 62
Melt Flow 29.4 g/10 min

@Load 2.16 kg,
Temperature 260 °C
29.4 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 63.0 MPa
9140 psi
50mm/min; ISO 527-2/1A
Elongation at Yield 4.5 %
4.5 %
50mm/min; ISO 527-2/1A
Tensile Modulus 2.60 GPa
377 ksi
1mm/min; ISO 527-2/1A
Charpy Impact Unnotched 2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.260 J/cm²

@Temperature 23.0 °C
1.24 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C
167 °F
ISO 75-1,-2
Vicat Softening Point 80.0 °C
176 °F
B50 (50°C/h 50N); ISO 306
Glass Transition Temp, Tg 78.0 °C
172 °F
10°C/min; ISO 11357-1,-2,-3
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Optical Properties Metric English Comments
Refractive Index 1.53
1.53
ISO 489
Transmission, Visible 91 %
91 %
ISO 13468-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Dielectric Constant 2.35

@Frequency 1000 - 10000 Hz
2.35

@Frequency 1000 - 10000 Hz
IEC 60250
Comparative Tracking Index >= 600 V
>= 600 V
IEC 60112
Processing Properties Metric English Comments
Feed Temperature <= 60.0 °C
<= 140 °F
Nozzle Temperature 220 - 250 °C
428 - 482 °F
Zone 1 190 - 220 °C
374 - 428 °F
Zone 2 200 - 230 °C
392 - 446 °F
Zone 3 210 - 240 °C
410 - 464 °F
Zone 4 220 - 250 °C
428 - 482 °F
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Injection Velocity 50.0 - 150 mm/sec
1.97 - 5.91 in/sec
Moderate to Fast
Injection Pressure 50.0 - 110 MPa
7250 - 16000 psi
Specific
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Specific
Back Pressure <= 15.0 MPa
<= 2180 psi
Specific
Screw Speed 50 - 200 rpm
50 - 200 rpm