Total EVA 1020 VN 3 Ethylene Vinyl Acetate Copolymer - Blown Film

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Total Atofina
Trade Name EVA
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total EVA 1020 VN 3 Ethylene Vinyl Acetate Copolymer - Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EVA 1020 VN 3 is made by a high pressure tubular process. Grade for flexible, very transparent films with high strength and very good sealability. Contains an antioxidant.Application examples: Thin shrink film for food packaging (coextrusion, lamination...), stretch film.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.929 g/cc
0.929 g/cc
ISO 1183
Vinyl Acetate Content 9.0 %
9.0 %
Thickness 40.0 microns
1.57 mil
for samples tested on this data sheet
20.0 - 100 microns
0.787 - 3.94 mil
possible range, depending on extrusion conditions
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.80 MPa
1130 psi
ISO 527-3
Film Tensile Strength at Yield, TD 6.50 MPa
943 psi
ISO 527-3
Film Elongation at Break, MD 380 %
380 %
ISO 527-3
Film Elongation at Break, TD 570 %
570 %
ISO 527-3
Modulus of Elasticity 0.100 GPa
14.5 ksi
ISO 527-2
Elmendorf Tear Strength, MD 3.10 g/micron
78.7 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 3.60 g/micron
91.4 g/mil
ISO 6383-2
Dart Drop Test 400 g
0.882 lb
ISO 7765-1
Film Tensile Strength at Break, MD 29.0 MPa
4210 psi
ISO 527-3
Film Tensile Strength at Break, TD 24.0 MPa
3480 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 97.0 °C
207 °F
ISO 11357
Vicat Softening Point 79.0 °C
174 °F
ISO 306
Optical Properties Metric English Comments
Haze 3.5 %
3.5 %
ISO 14782
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Processing Properties Metric English Comments
Processing Temperature 150 - 180 °C
302 - 356 °F