Total HDPE BM961 High Density Polyethylene, High Gloss Blow Molding Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer	Total Atofina
Trade Name	HDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total HDPE BM961 High Density Polyethylene, High Gloss Blow Molding Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyethylene: High density High Gloss Blow Molding ResinCharacteristics:High GlossHigh stiffnessGood abrasion resistanceFDA CompliantApplications:Coextruded glossy bottlesBlending agent for other polyethylenes to increase stiffness or to increase glossInformation provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.961 g/cc	0.961 g/cc	ASTM D792
ESCR 10% Igepal®	>= 10 hour	>= 10 hour	ASTM D1693, Cond. B
Melt Flow	1.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	33 g/10 min @Load 21.6 kg, Temperature 190 °C	33 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	29.6 MPa	4300 psi	ASTM D638
Elongation at Break	>= 500 %	>= 500 %	ASTM D638
Flexural Modulus	1.33 GPa	193 ksi	ASTM D790
Izod Impact, Notched	2.94 J/cm	5.50 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	129 °C	265 °F	ASTM D3417

Optical Properties	Metric	English	Comments
Gloss	>= 25 %	>= 25 %	at 60°; Total Method

Processing Properties	Metric	English	Comments
Melt Temperature	182 - 199 °C	360 - 390 °F	Extrusion