Total Lumicene® mPE M 3410 EP Metallocene Medium Density Film Resin (Unverified Data**)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Lumicene® mPE M 3410 EP Metallocene Medium Density Film Resin (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyethylene: Metallocene Medium Density Film ResinCharacteristics:Outstanding clarity and glossExcellent bubble stabilityHigh StiffnessGood puncture resistanceGood tear strengthGood heat sealing propertiesExcellent compatibility with LDPE and LLDPEApplications:Tissue & towel overwrap filmsClarity shrink filmsProtective packagingLaminationsMultilayer packaging filmInformation provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.934 g/cc	0.934 g/cc	ASTM D792
Water Vapor Transmission	10.1 g/m²/day	0.650 g/100 in²/day	ASTM E96/66
Thickness	25.4 microns	1.00 mil
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	30 g/10 min @Load 21.6 kg, Temperature 190 °C	30 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	400 %	400 %	ASTM D882, A
Film Elongation at Break, TD	650 %	650 %	ASTM D882, A
Coefficient of Friction	0.40	0.40	I/I; TOTAL Method
Elmendorf Tear Strength MD	55 g	55 g	ASTM D1922
Elmendorf Tear Strength TD	400 g	400 g	ASTM D1922
Dart Drop Test	60.0 g	0.132 lb	ASTM D1709, A
Film Tensile Strength at Break, MD	44.1 MPa	6400 psi	ASTM D882, A
Film Tensile Strength at Break, TD	42.1 MPa	6100 psi	ASTM D882, A
1% Secant Modulus, MD	365 MPa	53000 psi	ASTM D882, A
1% Secant Modulus, TD	386 MPa	56000 psi	ASTM D882, A
Heat Seal Strength Initiation Temperature	120 °C	248 °F	TOTAL Method

Thermal Properties	Metric	English	Comments
Melting Point	124 °C	255 °F	ASTM D3417

Optical Properties	Metric	English	Comments
Haze	9.0 %	9.0 %	ASTM D1003
Gloss	65 %	65 %	at 45°; ASTM D523

Processing Properties	Metric	English	Comments
Melt Temperature	193 - 210 °C	380 - 410 °F	Extrusion