Total PPH 3270 Polypropylene Homopolymer, High Crystallinity, Low Melt Flow Film Grade
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Total Atofina |
| Trade Name | PPH |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPH 3270 Polypropylene Homopolymer, High Crystallinity, Low Melt Flow Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low Residuals TOTAL Polypropylene 3270 utilizes the TOTAL Polypropylene proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock. 3270 is available with custom slip and antiblock packagesFDA. 3270 complies with all applicable FDA regulations for food contact use.Recommended Applications. TOTAL Polypropylene 3270 is recommended in orientation processes for manufacture of packaging tapes and films that benefit from improved stiffness and barrier protection.Information provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Water Vapor Transmission | 3.10 g/m²/day @Temperature 37.8 °C |
0.200 g/100 in²/day @Temperature 100 °F |
90% RH; ASTM F1249-90 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882 |
| Film Elongation at Break, TD | 60 % | 60 % | ASTM D882 |
| Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 269 MPa | 39000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 2900 MPa | 420000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 4830 MPa | 700000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | DSC |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 274 °C | 450 - 525 °F | Oriented Film Extrusion |
Users viewing this material also viewed the following:
- MV Labs PT800 PtO2·xH2O Platinum(IV) oxide hydrate
- Polymax® Maxelast® P2740 TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS (Europe-Africa-Middle East)
- Ravago Manufacturing Americas Hylon® N1013THL Nylon 6/6 (DAM)
- DSM Akulon® K224-G0 Nylon 6-50% Glass Reinforced (European Grade) (Cond)
- CIMBAR CAL-BEN™ Calcium Bentonite
- Axiall NR-5009 Rigid PVC, Molding
- G-2705 Styrene-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved