Total XSene® HD55110 High Density Polyethylene - Blown Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Total Atofina
Trade Name	XSene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total XSene® HD55110 High Density Polyethylene - Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HDPE HD55110 is a bimodal high density polyethylene with a particular molecular design developed with Total Petrochemicals Double Loop Technology™.HDPE HD55110 has been especially designed for applications where high film properties can be obtained both in pure, in blend or in coextrusion films.HDPE HD55110 can be used in high neck extrusion as well as low neck extrusion and is dedicated to several applications such as food packaging, lamination films, carrier bags, pouches, industrial packaging and hygiene packaging. Very thin films can also be easily achieved (down to 10 microns).Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.955 g/cc	0.955 g/cc	ISO 1183
Thickness	>= 10.0 microns	>= 0.394 mil
	12.0 microns	0.472 mil	for samples tested on this data sheet
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 190 °C	0.30 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
	11 g/10 min @Load 21.6 kg, Temperature 190 °C	11 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	39.0 MPa	5660 psi	ISO 527-3
Film Tensile Strength at Yield, TD	30.0 MPa	4350 psi	ISO 527-3
Film Elongation at Break, MD	308 %	308 %	ISO 527-3
Film Elongation at Break, TD	460 %	460 %	ISO 527-3
Elmendorf Tear Strength, MD	0.600 g/micron	15.2 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	4.60 g/micron	117 g/mil	ISO 6383-2
Dart Drop Test	170 g	0.375 lb	ISO 7765-1
Film Tensile Strength at Break, MD	64.0 MPa	9280 psi	ISO 527-3
Film Tensile Strength at Break, TD	54.0 MPa	7830 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	132 °C	270 °F	ISO 11357
Vicat Softening Point	130 °C	266 °F	ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	180 - 230 °C	356 - 446 °F