Toyobo GLAMIDE® T-402 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-402 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-402 is a GF reinforced Nylon-6. It contains 30% GF.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 1.3 % | 1.3 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0040 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0040 - 0.0070 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 19 g/10 min | 19 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 70.0 MPa @Temperature 80.0 °C |
10200 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 |
| 100 MPa @Temperature 80.0 °C |
14500 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 105 MPa @Temperature 23.0 °C |
15200 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| 170 MPa @Temperature 23.0 °C |
24700 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 220 MPa @Temperature -40.0 °C |
31900 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| 245 MPa @Temperature -40.0 °C |
35500 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.6 % | 3.6 % | Absolute Drying; ASTM-D638 |
| 5.6 % | 5.6 % | Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| Flexural Strength | 100 MPa @Temperature 80.0 °C |
14500 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 |
| 130 MPa @Temperature 23.0 °C |
18900 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 150 MPa @Temperature 80.0 °C |
21800 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 260 MPa @Temperature 23.0 °C |
37700 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 290 MPa @Temperature -40.0 °C |
42100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 305 MPa @Temperature -40.0 °C |
44200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 3.40 GPa @Temperature 80.0 °C |
493 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 |
| 4.50 GPa @Temperature 80.0 °C |
653 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 5.00 GPa @Temperature 23.0 °C |
725 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 8.50 GPa @Temperature 23.0 °C |
1230 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 9.20 GPa @Temperature -40.0 °C |
1330 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 10.8 GPa @Temperature -40.0 °C |
1570 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 155 MPa | 22500 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.800 J/cm @Temperature -40.0 °C |
1.50 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.850 J/cm @Temperature -40.0 °C |
1.59 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D256 | |
| 1.20 J/cm @Temperature 23.0 °C |
2.25 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 2.00 J/cm @Temperature 23.0 °C |
3.75 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.5%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 2.00 mm |
432 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.5%); ASTM-D149 |
| 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 90 sec | 90 sec | Practical Use (Water Absorption 2.5%); ASTM-D495 |
| 100 sec | 100 sec | Absolute Drying; ASTM-D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |