Toyobo GLAMIDE® T-663G50A MXD66
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-663G50A MXD66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-663G50A is a GF reinforced, aromatic MXD66 nylon. It has a good appearance and contains 50% GF.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 50 % | 50 % | |
| Water Absorption | 0.30 % | 0.30 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0060 - 0.0080 cm/cm @Thickness 3.00 mm |
0.0060 - 0.0080 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 100 MPa @Temperature 80.0 °C |
14500 psi @Temperature 176 °F |
Practical Use (Water Absorption 0.8%); ASTM-D638 |
| 112 MPa @Temperature 80.0 °C |
16200 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 165 MPa @Temperature 23.0 °C |
23900 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D638 | |
| 220 MPa @Temperature 23.0 °C |
31900 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 245 MPa @Temperature -40.0 °C |
35500 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D638 | |
| 270 MPa @Temperature -40.0 °C |
39200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 2.0 % | 2.0 % | Absolute Drying; ASTM-D638 |
| 2.2 % | 2.2 % | Practical Use (Water Absorption 0.8%); ASTM-D638 | |
| Flexural Strength | 155 MPa @Temperature 80.0 °C |
22500 psi @Temperature 176 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 |
| 175 MPa @Temperature 80.0 °C |
25400 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 260 MPa @Temperature 23.0 °C |
37700 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 330 MPa @Temperature -40.0 °C |
47900 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 345 MPa @Temperature 23.0 °C |
50000 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 360 MPa @Temperature -40.0 °C |
52200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 5.90 GPa @Temperature 80.0 °C |
856 ksi @Temperature 176 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 |
| 7.00 GPa @Temperature 80.0 °C |
1020 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 12.5 GPa @Temperature 23.0 °C |
1810 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 15.0 GPa @Temperature 23.0 °C |
2180 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 15.1 GPa @Temperature -40.0 °C |
2190 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 16.0 GPa @Temperature -40.0 °C |
2320 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 180 MPa | 26100 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 1.40 J/cm @Temperature -40.0 °C |
2.62 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 1.50 J/cm @Temperature -40.0 °C |
2.81 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D256 | |
| 1.70 J/cm @Temperature 23.0 °C |
3.18 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 1.90 J/cm @Temperature 23.0 °C |
3.56 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C | 10.0 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | Practical Use (Water Absorption 0.8%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 0.8%); ASTM-D149 |
| 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 33 sec | 33 sec | Practical Use (Water Absorption 0.8%); ASTM-D495 |
| 40 sec | 40 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 550 V | 550 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Injection Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |