Toyobo GLAMIDE® T-777-02 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-777-02 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-777-02 is a standard plating grade, mineral-reinforced Nylon-6.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 40 % | 40 % | |
| Water Absorption | 0.90 % | 0.90 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Thickness 1.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0080 - 0.013 cm/cm @Thickness 3.00 mm |
0.0080 - 0.013 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 33 g/10 min | 33 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 |
| 40.0 MPa @Temperature 80.0 °C |
5800 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| 86.0 MPa @Temperature 23.0 °C |
12500 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| 115 MPa @Temperature -40.0 °C |
16700 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 11 % | 11 % | Absolute Drying; ASTM-D638 |
| 25 % | 25 % | Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| Flexural Strength | 38.0 MPa @Temperature 80.0 °C |
5510 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 |
| 60.0 MPa @Temperature 80.0 °C |
8700 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 65.0 MPa @Temperature -40.0 °C |
9430 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 75.0 MPa @Temperature 23.0 °C |
10900 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 140 MPa @Temperature 23.0 °C |
20300 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 170 MPa @Temperature -40.0 °C |
24700 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 1.00 GPa @Temperature 80.0 °C |
145 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 |
| 1.70 GPa @Temperature 80.0 °C |
247 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 5.50 GPa @Temperature 23.0 °C |
798 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 6.30 GPa @Temperature -40.0 °C |
914 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 7.30 GPa @Temperature -40.0 °C |
1060 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 105 MPa | 15200 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.320 J/cm @Temperature -40.0 °C |
0.599 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.450 J/cm @Temperature -40.0 °C |
0.843 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D256 | |
| 0.650 J/cm @Temperature 23.0 °C |
1.22 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 2.80 J/cm @Temperature 23.0 °C |
5.25 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C | 38.9 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.0%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 2.00 mm |
406 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.0%); ASTM-D149 |
| 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 120 sec | 120 sec | Practical Use (Water Absorption 2.0%); ASTM-D495 |
| 130 sec | 130 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Injection Pressure | 40.0 - 50.0 MPa | 5800 - 7250 psi |