Toyobo GLAMIDE® TY-145TZ Nylon-6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer Toyobo
Trade Name GLAMIDE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Toyobo GLAMIDE® TY-145TZ Nylon-6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-145TZ is a mineral-reinforced Nylon-6 with smooth fluidity.25
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
Absolute Drying; ASTM-D792
Filler Content 25 %
25 %
Water Absorption 0.80 %
0.80 %
Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium 2.7 %
2.7 %
Absolute Drying; ASTM-D570
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 1.00 mm
0.0020 - 0.0030 in/in

@Thickness 0.0394 in
Absolute Drying
0.0040 - 0.0080 cm/cm

@Thickness 3.00 mm
0.0040 - 0.0080 in/in

@Thickness 0.118 in
Absolute Drying
Melt Flow 15 g/10 min
15 g/10 min
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
Absolute Drying; ASTM-D785
Tensile Strength, Ultimate 36.0 MPa

@Temperature 80.0 °C
5220 psi

@Temperature 176 °F
Practical Use (Water Absorption 2.7%); ASTM-D638
45.0 MPa

@Temperature 80.0 °C
6530 psi

@Temperature 176 °F
Absolute Drying; ASTM-D638
58.0 MPa

@Temperature 23.0 °C
8410 psi

@Temperature 73.4 °F
Practical Use (Water Absorption 2.7%); ASTM-D638
85.0 MPa

@Temperature 23.0 °C
12300 psi

@Temperature 73.4 °F
Absolute Drying; ASTM-D638
102 MPa

@Temperature -40.0 °C
14800 psi

@Temperature -40.0 °F
Practical Use (Water Absorption 2.7%); ASTM-D638
107 MPa

@Temperature -40.0 °C
15500 psi

@Temperature -40.0 °F
Absolute Drying; ASTM-D638
Elongation at Break 5.0 %
5.0 %
Absolute Drying; ASTM-D638
8.0 %
8.0 %
Practical Use (Water Absorption 2.7%); ASTM-D638
Flexural Strength 53.0 MPa

@Temperature 80.0 °C
7690 psi

@Temperature 176 °F
Practical Use (Water Absorption 2.7%); ASTM-D790
78.0 MPa

@Temperature 80.0 °C
11300 psi

@Temperature 176 °F
Absolute Drying; ASTM-D790
93.0 MPa

@Temperature 23.0 °C
13500 psi

@Temperature 73.4 °F
Practical Use (Water Absorption 2.7%); ASTM-D790
140 MPa

@Temperature 23.0 °C
20300 psi

@Temperature 73.4 °F
Absolute Drying; ASTM-D790
158 MPa

@Temperature -40.0 °C
22900 psi

@Temperature -40.0 °F
Practical Use (Water Absorption 2.7%); ASTM-D790
168 MPa

@Temperature -40.0 °C
24400 psi

@Temperature -40.0 °F
Absolute Drying; ASTM-D790
Flexural Modulus 1.50 GPa

@Temperature 80.0 °C
218 ksi

@Temperature 176 °F
Practical Use (Water Absorption 2.7%); ASTM-D790
3.70 GPa

@Temperature 80.0 °C
537 ksi

@Temperature 176 °F
Absolute Drying; ASTM-D790
4.60 GPa

@Temperature 23.0 °C
667 ksi

@Temperature 73.4 °F
Practical Use (Water Absorption 2.7%); ASTM-D790
6.80 GPa

@Temperature 23.0 °C
986 ksi

@Temperature 73.4 °F
Absolute Drying; ASTM-D790
7.00 GPa

@Temperature -40.0 °C
1020 ksi

@Temperature -40.0 °F
Practical Use (Water Absorption 2.7%); ASTM-D790
8.00 GPa

@Temperature -40.0 °C
1160 ksi

@Temperature -40.0 °F
Absolute Drying; ASTM-D790
Compressive Strength 66.0 MPa
9570 psi
Practical Use (Water Absorption 2.7%); ASTM-D695
97.0 MPa
14100 psi
Absolute Drying; ASTM-D695
Izod Impact, Notched 0.540 J/cm

@Temperature -40.0 °C
1.01 ft-lb/in

@Temperature -40.0 °F
Absolute Drying; ASTM-D256
0.680 J/cm

@Temperature -40.0 °C
1.27 ft-lb/in

@Temperature -40.0 °F
Practical Use (Water Absorption 2.7%); ASTM-D256
0.800 J/cm

@Temperature 23.0 °C
1.50 ft-lb/in

@Temperature 73.4 °F
Absolute Drying; ASTM-D256
2.60 J/cm

@Temperature 23.0 °C
4.87 ft-lb/in

@Temperature 73.4 °F
Practical Use (Water Absorption 2.7%); ASTM-D256
Taber Abrasion, mg/1000 Cycles 30
30
CS-17, Absolute Drying; ASTM-D1044
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C
30.6 µin/in-°F
Absolute Drying; ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi) 207 °C
405 °F
Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Absolute Drying; ASTM-D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 ohm-cm
1.00e+9 ohm-cm
Practical Use (Water Absorption 2.7%); ASTM-D257
1.00e+12 ohm-cm
1.00e+12 ohm-cm
Absolute Drying; ASTM-D257
Dielectric Strength 17.0 kV/mm

@Thickness 2.00 mm
432 kV/in

@Thickness 0.0787 in
Practical Use (Water Absorption 2.7%); ASTM-D149
25.0 kV/mm

@Thickness 2.00 mm
635 kV/in

@Thickness 0.0787 in
Absolute Drying; ASTM-D149
Arc Resistance 120 sec
120 sec
Practical Use (Water Absorption 2.7%); ASTM-D495
130 sec
130 sec
Absolute Drying; ASTM-D495
Comparative Tracking Index >= 600 V
>= 600 V
IEC Method
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection Pressure 30.0 - 60.0 MPa
4350 - 8700 psi