Toyobo VYLOPET® CA3300 PC/PBT Polymer Alloy, Impact Resistant, Chemical Resistant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® CA3300 PC/PBT Polymer Alloy, Impact Resistant, Chemical Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Lamp partsHome electric appliance partsFeatures: Fine appearanceSurface lusterImpact resistantChemical resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs at 23°C; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.00 mm |
0.0070 in/in @Thickness 0.118 in |
MD |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.00 mm |
0.0070 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 140 % | 140 % | ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | Molding temperature |
| Mold Temperature | 70.0 °C | 158 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 3 hour | 3 hour |
Users viewing this material also viewed the following:
- Oceanchem Group Triethyl Phosphate (TEP)
- Ineos Nova 1552 High Performance Styrenic Enhanced Polystyrene (discontinued **)
- Nitriflex N-6420 NBR / PVC
- Overview of materials for Medium Density Polyethylene (MDPE), Film Grade
- Saint-Gobain COHRlastic® 9040 Wide Series General Purpose Silicone Solid Rubber
- Techmer ES Luriblend® PSU GF20 TL5 20% Glass Filled
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
- China-Yixing Longly Refractories Steatite Ceramics (High Frequency Porcelain)
- Solvay Specialty Polymers Ixef® 1313/0004 Polyarylamide, 40% Glass Fiber + Elastomer, DAM (discontinued **)&l
Copyright © lookpolymers.com All Rights Reserved